翻訳と辞書 Words near each other ・ Compsocerus parviscopus ・ Compsocerus proximus ・ Compression Networks ・ Compression of Genomic Re-Sequencing Data ・ Compression of morbidity ・ Compression ratio ・ Compression release ・ Compression release engine brake ・ Compression seal fitting ・ Compression set ・ Compression stockings ・ Compression Systems ・ Compression theorem ・ Compression therapy ・ Compression virus ・ Compressive strength ・ Compressor ・ Compressor (software) ・ Compressor characteristic ・ Compressor map ・ Compressor stall ・ Compressor station ・ Compressor Station Number 10 STOLport ・ Compressorhead ・ Comprido River (São Paulo) ・ Comprimario ・ Comprise ・ Comprised of ・ Compromis ・ Compromise Dictionary Lists mini英和辞書 mini和英辞書 Webster 1913 Latin-English FOLDOC Wikipedia English ウィキペディア

翻訳と辞書　辞書検索 [ 開発暫定版 ] スポンサード リンク Compressive strength ： ウィキペディア英語版 Compressive strength In the study of strength of materials, the compressive strength is the capacity of a material or structure to withstand loads tending to reduce size. It can be measured by plotting applied force against deformation in a testing machine. Some materials fracture at their compressive strength limit; others deform irreversibly, so a given amount of deformation may be considered as the limit for compressive load. Compressive strength is a key value for design of structures. Compressive strength is often measured on a universal testing machine; these range from very small table-top systems to ones with over 53 MN capacity. Measurements of compressive strength are affected by the specific test method and conditions of measurement. Compressive strengths are usually reported in relationship to a specific technical standard. == Introduction == When a specimen of material is loaded in such a way that it extends it is said to be in tension. On the other hand if the material compresses and shortens it is said to be in compression. On an atomic level, the molecules or atoms are forced apart when in tension whereas in compression they are forced together. Since atoms in solids always try to find an equilibrium position, and distance between other atoms, forces arise throughout the entire material which oppose both tension or compression. The phenomena prevailing on an atomic level are therefore similar. The "strain" is the relative change in length under applied stress; positive strain characterises an object under tension load which tends to lengthen it, and a compressive stress that shortens an object gives negative strain. Tension tends to pull small sideways deflections back into alignment, while compression tends to amplify such deflection into buckling. Compressive strength is measured on materials, components, and structures. By definition, the ultimate compressive strength of a material is that value of uniaxial compressive stress reached when the material fails completely. The compressive strength is usually obtained experimentally by means of a compressive test. The apparatus used for this experiment is the same as that used in a tensile test. However, rather than applying a uniaxial tensile load, a uniaxial compressive load is applied. As can be imagined, the specimen (usually cylindrical) is shortened as well as spread laterally. A Stress–strain curve is plotted by the instrument and would look similar to the following: The compressive strength of the material would correspond to the stress at the red point shown on the curve. In a compression test, there is a linear region where the material follows Hooke's Law. Hence for this region ''$\backslash sigma=E\backslash epsilon$'' where this time E refers to the Young's Modulus for compression. In this region, the material deforms elastically and returns to its original length when the stress is removed. This linear region terminates at what is known as the yield point. Above this point the material behaves plastically and will not return to its original length once the load is removed. There is a difference between the engineering stress and the true stress. By its basic definition the uniaxial stress is given by: $\backslash sigma\; =\; \backslash frac$ where, F = Load applied (), A = Area () As stated, the area of the specimen varies on compression. In reality therefore the area is some function of the applied load i.e. A = f(F). Indeed, stress is defined as the force divided by the area at the start of the experiment. This is known as the engineering stress and is defined by, $\backslash sigma\_e\; =\; \backslash frac$ A0=Original specimen area () Correspondingly, the engineering strain would be defined by: $\backslash epsilon\_e\; =\; \backslash frac$ where l = current specimen length () and l0 = original specimen length () The compressive strength would therefore correspond to the point on the engineering stress strain curve $(\backslash epsilon\_e^$ *,\sigma_e^ *) defined by $\backslash sigma\_e^$ * = \frac $\backslash epsilon\_e^$ * = \frac where F * = load applied just before crushing and l * = specimen length just before crushing. 抄文引用元・出典: フリー百科事典『 ウィキペディア（Wikipedia）』 ■ウィキペディアで「Compressive strength」の詳細全文を読む スポンサード リンク 翻訳と辞書 : 翻訳のためのインターネットリソース Copyright(C) kotoba.ne.jp 1997-2016. All Rights Reserved.